J Dent. 2021 May 30:103708. doi: 10.1016/j.jdent.2021.103708. Online ahead of print.
ABSTRACT
OBJECTIVES: To investigate the effect of rapid high-intensity light-curing on the marginal integrity of four bulk-fill composites, including two materials specifically designed for high-intensity curing.
METHODS: Class V cavities were prepared on buccal surfaces of intact human molars with simulated pulpal pressure, filled in a single increment and light-cured using a conventional (10 s @ 1,340 mW/cm2) or high-intensity (3 s @ 3,440 mW/cm2) protocol. The restorations were subjected to thermo-mechanical loading (TML) comprising 1,200,000 mechanical loading cycles and 3,000 thermocycles. Quantitative margin analysis was performed before and after TML using a scanning electron microscope, and the marginal integrity was expressed as percentage of continuous margin (PCM).
RESULTS: All PCM values measured before TML were statistically similar regardless of the material and curing protocol (p>0.05). A statistically significant effect of the curing protocol (p=0.021) was identified only after TML for one material. PCM was significantly diminished by TML (p<0.001) for most combinations of material and curing protocol. The PCM values of the sculptable composites after TML were statistically similar regardless of the curing protocol (p>0.05). Compared to these values, significantly lower PCM after TML was identified for the flowable composites cured with the high-intensity protocol (p=0.001-0.045).
CONCLUSION: In most cases, high-intensity and conventional curing generally led to similar marginal integrity. Although all of the investigated composites initially performed similarly well, the flowable composites light-cured using the high-intensity protocol showed a significantly inferior marginal integrity compared to the sculptable composites after loading.
CLINICAL SIGNIFICANCE: Rapid high-intensity light-curing cannot be recommended for flowable bulk-fill composites since it may compromise the tooth-restoration interface.
PMID:34077801 | DOI:10.1016/j.jdent.2021.103708