Dent Mater J. 2023 Jun 3. doi: 10.4012/dmj.2022-230. Online ahead of print.
ABSTRACT
The purpose of the present study is to evaluate the fracture resistance and the fit of CAD-CAM produced inlay-retained fixed partial dentures. Eighteen experimental groups were generated according to different CAD-CAM ceramic materials (zirconia, lithium disilicate, and zirconia-reinforced lithium silicate), different connector dimensions (12, 14, and 16 mm2), and application of thermomechanical-aging (1,200,000 cycles of cyclic loading with simultaneous thermal cycling). Gap values of thermomechanically-aged groups were measured by using periapical radiographs. Then, the specimens were tested for fracture resistance and failure types were examined. The results were statistically analyzed (α=0.05). Higher gap values were observed after aging. Zirconia showed the highest fracture resistance values among the most of the experimental groups. In non-aged groups, the most frequent failure type was decementation in zirconia group. In the aged groups, the most frequent failure type was molar connector fracture. Thermomechanical-aging increased the gap values and decreased the fracture resistance values.
PMID:37271542 | DOI:10.4012/dmj.2022-230