J Prosthodont. 2023 Oct 12. doi: 10.1111/jopr.13783. Online ahead of print.
ABSTRACT
PURPOSE: To compare the effect of different pre-cementation surface treatments and bonding protocols on the retention force of additively manufactured (AM) implant-supported interim crowns.
MATERIAL AND METHODS: A total of 50 AM interim crowns (Temporary CB resin) were cemented on implant abutments. Five groups (n = 10) were established based on the different surface pre-treatments performed in the intaglio surface of the specimens: no surface pre-treatment (Group C or control), air-abraded with 50-μm aluminium oxide particles (Group AP), air-abraded with 50-μm aluminium oxide particles followed by the application of silane (Group AMP), silane (Group MP), and air-abraded with 30μm silica-coated aluminum oxide particles followed by the application of silane (Group CMP). Each specimen was cemented into an implant abutment using a composite resin cement (Rely X Unicem2). Afterward, the specimens underwent retention testing with a Universal Instron machine. Pull-off forces (N) and modes of failure were registered. Statistical analysis was performed using Mann-Whitney U tests with Bonferroni corrections for multiple tests (α = .05).
RESULTS: The median retention force values were 233.27 ±79.28 N for Group Control, 398.59 ±68.59 N for Group MP, 303.21 ±116.80 N for Group AMP, 349.31 ±167.73 N for Group CMP, and 219.85 ± 55.88 N for Group AP. The pull-off forces were significantly greater for Group MP, while the differences between the remaining groups were not statistically significant (P>0.05). Group AP showed the lowest retention force values among all the groups. Failure modes after the pull-off testing were predominantly adhesive and substrate failure of the AM interim material.
CONCLUSIONS: The surface treatment of the intaglio AM crown tested significantly influenced the retention force values measured. Pre-treatment with an MDP-containing silane improved the retentive force values computed, whereas pre-treatment with 50-μm Al2 O3 air-particle abrasion alone is not recommended prior to cementation on a titanium-based implant abutment. This article is protected by copyright. All rights reserved.
PMID:37823323 | DOI:10.1111/jopr.13783