Saudi Dent J. 2025 Apr 15;37(1-3):3. doi: 10.1007/s44445-025-00002-5.
ABSTRACT
Adhesives are essential for attaching orthodontic brackets to the tooth surface and ensuring safe removal during debonding. ACTIVA™ BioACTIVE-Restorative (ABR) is a bioactive composite with potential advantages. The purpose of this study was to evaluate the shear bond strength (SBS) and adhesive remnant index (ARI) of ACTIVA™ BioACTIVE-Restorative (ABR) with conventional adhesives, including Transbond XT™ (TXT) and Orthocem™ (OC). A total of 51 human maxillary premolars were distributed randomly into three groups (n = 17). Each group was bonded with one adhesive following the manufacturer’s protocols. Then were subjected to 5000 thermocycles to simulate oral conditions. SBS was measured using a universal testing machine, and ARI scores were visually analysed under magnification. Statistical analysis was conducted using one-way ANOVA and chi-squared tests, with a 0.05 level of significance. Mean SBS values were 11.26 MPa, 12.52 MPa, and 12.96 MPa for ABR, TXT, and OC, respectively, with no significant differences (p = 0.513). ARI analysis revealed significant differences (p = 0.009) as ABR predominantly exhibited ARI 3 scores, indicating no adhesive remnants on enamel. In contrast, TXT and OC groups showed higher adhesive retention. ABR demonstrated shear bond strength comparable to conventional adhesives, meeting the clinical thresholds for orthodontic use. But demonstrated more complete adhesive failure in the enamel-adhesive interface rather than cohesive failure within the adhesive material like in TXT and OC.
PMID:40397265 | DOI:10.1007/s44445-025-00002-5