J Prosthodont Res. 2021 Mar 25. doi: 10.2186/jpr.JPR_D_20_00251. Online ahead of print.
ABSTRACT
PURPOSE: The aim of this study was to clarify the effects of different bonding systems (BSs) with various polymerization modes and root canal regions on the bond strength of core build-up resin composite to dentin.
METHODS: Post cavities were prepared in the roots of 54 bovine teeth. Three types of BS with various polymerization modes (light, chemical, and dual-cure) were applied to the walls of the cavities, which were subsequently filled with core build-up resin composite, and stored in 37ºC water for 7 days. Each tooth was then sectioned perpendicular to the long axis of the tooth into 9-disk from the coronal to the apical side. Bond strengths were measured on two-thirds of the disks, while dye penetration was examined in the remaining third.
RESULTS: Statistical analysis revealed significant differences between the bond strengths of BSs with different polymerization modes, indicating chemical-cured BS had higher bond strength than light-cured BS. The chemical-cured BS group showed cohesive failure in both resin composite and dentin regardless of the root canal region, while adhesive failure was observed in the coronal region for dual-cured BS and in the apical region for light-cured BS. Dye penetration was significantly more at the bonding interface at the apical region of the light-cured BS.
CONCLUSIONS: Chemical-cured BS displayed a greater bond strength than light-cured BS. Cohesive failure was observed in both core build-up resin and dentin, indicating that the integration of tooth structure with resin composite was effective for retaining the resin core and sealing the root canal.
PMID:33762506 | DOI:10.2186/jpr.JPR_D_20_00251