J Oral Sci. 2022 Aug 19. doi: 10.2334/josnusd.22-0147. Online ahead of print.
ABSTRACT
PURPOSE: To evaluate the effect of different surface treatments, ferrule heights, and luting agents on the pull-out bond strength (PBS) of computer-aided design/computer-aided manufacturing (CAD-CAM) monolithic endocrowns.
METHODS: After endodontic treatment and preparation for two endocrown designs (ferrule height 0 mm or 2 mm), CAD-CAM monolithic zirconia endocrowns were fabricated for 80 mandibular molars. Each endocrown design group was then divided on the basis of surface treatment into two groups: half were air-abraded and half were air-abraded/laser-irradiated. Then, all treated groups were further divided into two subgroups (n = 10) and cemented to teeth with either a 10-methacryloyloxydecyl dihydrogen phosphate (MDP)-containing resin luting agent (Panavia SA) or a combination of MDP-containing primer and MDP-free resin luting agent (Monobond Plus/Multilink Automix). PBS was measured with a universal test machine after simulated chewing and thermocycling. Three-way ANOVA and the post-hoc Bonferroni test were used for statistical analysis.
RESULTS: PBS was significantly associated with type of surface treatment, type of luting agent, and ferrule height. Air-abraded/laser-irradiated endocrowns with a 2-mm ferrule that were cemented with Monobond Plus/Multilink Automix had the highest PBS (P < 0.05).
CONCLUSION: Surface treatment with air abrasion/laser irradiation, presence of a ferrule, and priming with an MDP-containing primer increased the PBS of monolithic zirconia endocrowns.
PMID:35989297 | DOI:10.2334/josnusd.22-0147