J Esthet Restor Dent. 2022 Sep 4. doi: 10.1111/jerd.12960. Online ahead of print.
ABSTRACT
OBJECTIVE: To compare the color stability, translucency, and biaxial flexural strength (BFS) of differently glazed advanced lithium disilicate (ALDS) with those of lithium disilicate (LDS) and zirconia-reinforced lithium silicate (ZLS) after coffee thermocycling.
MATERIALS AND METHODS: Forty disk-shaped specimens were prepared from three lithium silicate based materials (CEREC Tessera, ALDS; IPS e.max CAD, LDS; Vita Suprinity, ZLS). ALDS specimens were divided into two subgroups according to glazing procedures (reduced glaze duration, ALDS-S and normal glaze duration, ALDS-N), while LDS and ZLS specimens were crystallized and glazed. Color coordinate measurements were performed before and after coffee thermocycling. Color differences (ΔE00 ) and relative translucency parameters (RTP) were calculated. Specimens were then subjected to BFS test. Statistical analysis was performed by using 1- (ΔE00 and BFS) and 2-way (RTP) ANOVA tests (α = 0.05).
RESULTS: ΔE00 values of tested materials were similar (df = 3, F = 0.150, p = 0.929). Two-way ANOVA showed the significant effect of material type, coffee thermocycling, and the interaction between these parameters on RTP values (p < 0.001). Both before and after thermocycling, LDS had the highest (p ≤ 0.001) and ZLS had the lowest (p < 0.001) RTP values, while ALDS-N had higher RTP than ALDS-S (p ≤ 0.001). Among tested materials, only LDS had similar RTP values before and after thermocycling (p = 0.865) as the other materials had lower RTP values after thermocycling (p < 0.001). ALDS-N had higher BFS values than ALDS-S (p = 0.005), while LDS had similar values to ALDS specimens (p ≥ 0.201). ZLS had the highest BFS (p ≤ 0.007).
CONCLUSIONS: ALDS had comparable values to those of other materials. However, reduced glazing duration resulted in decreased translucency and BFS of ALDS.
CLINICAL SIGNIFICANCE: ALDS may be an appropriate restorative material for those patients with increased coffee consumption considering its color stability and ability to maintain translucency, particularly when glazed by using a conventional porcelain furnace.
PMID:36057856 | DOI:10.1111/jerd.12960